Electronics Forum | Thu Aug 01 12:55:41 EDT 2002 | johnw
we run the paste in both air and n2 depending on customer requirements again it run's fairly well in both. Some people say it's better sme say it doesn't make a bit of difference, I'm somewhere in between at the moment. I definately think there's imp
Electronics Forum | Wed May 24 15:59:34 EDT 2006 | JohnM
I have a product with mixed in Pb free and Pb BGAs. I decide to use SnPb paste with Pb free reflow profile to make it work for both types of BGA. Do I have a reliability solder joint issue by using this method? How is your opinion on this case? Can
Electronics Forum | Sat Aug 29 08:43:35 EDT 1998 | Dave F
| Hi, Friends, | Could you please recommend me some solder mask materials and equitements for high quality solder mask? Details such as company name, phone numer et al are welcomed. Thanks! | Have a good day | Xingsheng Xingsheng: Consider the follo
Electronics Forum | Tue Aug 31 17:36:36 EDT 2004 | davef
NO-LEAD COMPONENTS WITH LEAD SOLDER ISSUE: We agree with Russ. We've dicussed this several times on SMTnet. For instance, look here http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=25394 LEAD COMPONENTS WITH NO-LEAD SOLDER ISSUE: We disa
Electronics Forum | Wed Jul 07 13:41:42 EDT 1999 | Dave F
snip | | If you go for plugging be sure you have a protrusion spec that you can live with. This often results in little bumps of epoxy that can interfere with component placement. For us, tenting .015 vias usually gets us about 80% coverage from
Electronics Forum | Wed Jul 07 09:47:41 EDT 1999 | Peter Brant
| | Q #1) Is it more reliable to have the mask tent over the vias or risk getting vias half filled with solder? These are vias with an .020" hole and .040" or .050" pad. WIth regards to this question, and scott's follow up, I have used the "epoxy me
Electronics Forum | Wed Jul 07 10:25:13 EDT 1999 | John Thorup
| | Q #1) Is it more reliable to have the mask tent over the vias or risk getting vias half filled with solder? These are vias with an .020" hole and .040" or .050" pad. | | John, | It depends......mainly on the via size. Tenting works on smaller vi
Electronics Forum | Fri Feb 03 16:40:24 EST 2006 | Mike
At my last employer, we ran a number of tests to make a "Hybrid" profile work (same profile Joe lists) . It worked great for everything but BGAs. The problem (6 months ago) was using parts not rated for lead free reflow temps. As the market fills wit
Electronics Forum | Wed Feb 01 06:02:59 EST 2006 | joe
Hi, SAC BGA's in a SnPb reflow process can be achieved by ensuring the temp. on the BGA is at a peak min of 220�C and a time above 207-210�C for 60 - 90 Sec. Lower temperatures have shown incomplete mixing of alloys and some voiding.
Electronics Forum | Thu Sep 28 15:57:49 EDT 2000 | Chris
Donna, Please email me at nolefthere@yahoo.com and I will give you my work #. I would like to talk to you on this subject. I have been placing 0402s with a Contact 3AV machine since Nov 96. I have too many suggestions and comments to tell you her